Major Alloy Characteristics
ZAMAK 2: This is the strongest and hardest ZAMAK alloy. Generally die cast, it is occasionally employed for gravity casting. ZAMAK 2 is not the widely used.
ZAMAK 3: This is the most used general purpose zinc die casting alloy, providing an excellent combination of strength, ductility and impact strength. It also provides excellent plating and finishing characteristics. This alloy is the designer's first choice for die casting applications.
ZAMAK 5: ZAMAK 5 should be considered when moderately greater hardness, strength and creep resistance over ZAMAK 3 is required.
ZAMAK 7: this is a high purity for of ZAMAK 3 with similar mechanical properties. However, ZAMAK 7 has higher ductility (for forming bending operations) and the highest casting fluidity of the ZAMAK family.
ZA-8: This should be the first choice when considering die casting the ZA family, due to its cost effective hot chamber castability. ZA-8 provides improved performance characteristics over the ZAMAK alloys. Plating and finishing characteristics are similar. ZA-8 can also be sand or permanent mold cast.
ZA-12: This is the preferred alloy for permanent mold applications, although it can also be cal-chamber die cast with excellent results. It combines low temperature melting efficiency and thin wall capabilities with premium mechanical properties. ZA-12 should be used when switching from cast iron or permanent molded aluminum. ZA-21 can usually be poured directly into molds designed for aluminum and brass.
ZA-27: Components requiring optimum strength, hardness and light weight should be specified using ZA-27. With over double the yield strength of die cast A380 aluminum and 25% lighter than ZAMAK 3, this is definitely the high performance member of the group. ZA-27 also offers excellent bearing properties, comparable to those of aluminum-bronze.
EZAC: Eastern Alloy's newest commercially available alloy. EZAC is the strongest, hardest and most creep resistant die casting alloy available, and can be cast in the "hot-chamber" die casting process.
Zamak 4 was developed for the Asian markets to reduce the effects of die soldering while maintaining the ductility of zamak 3. This was achieved by using half the amount of copper from the zamak 5 composition.
Zamak 4 composition per standard
|Ningbo Jinyi Alloy Material Co.||min||3.9||0.3||0.03||-||-||-||-||-||-||-||-|
|Genesis Alloys Ltd.||min||3.9||0.3||0.04||-||-||-||-||-||-||-||-|
Zamak 4 properties
|Property||Metric value||Imperial value|
|Ultimate tensile strength||317 MPa||46,000 psi|
|Yield strength (0.2% offset)||221—269 MPa||32,000—39,000 psi|
|Impact strength||61 J (7 J aged)||45 ft-lbf (5 ft-lbf aged)|
|Shear strength||214—262 MPa||31,000—38,000 psi|
|Compressive yield strength||414—600 MPa||60,000—87,000 psi|
|Fatigue strength (rotary bending 5x108 cycles)||48—57 MPa||7,000—8,300 psi|
|Solidification range (melting range)||380—386 °C||716—727 °F|
|Density||6.6 g/cm3||0.24 lb/in3|
|Coefficient of thermal expansion||27.4 μm/m-°C||15.2 μin/in-°F|
|Thermal conductivity||108.9—113.0 W/m-K @ 100 °C||755.6—784.0 BTU-in/hr-ft2-°F @ 212 °F|
|Electrical conductivity||26-27% IACS|
|Specific heat capacity||418.7 J/kg-°C||0.100 BTU/lb-°F|