Product Details:
|
| Material: | Zinc Alloy (Zamak) | Model: | D051 |
|---|---|---|---|
| Size: | 46 X 17.5cm | Color: | Gold |
| Optional Color: | Gold,Silver,Antique Bronze And Antique Copper | ||
| Highlight: | cross crucifix,christian crucifix |
||
| Packaging Details: | 1pc/ bag, 200pcs/carton |
|---|---|
| Delivery Detail: | 35 days |
Coffin decoration
Material : zinc alloy
Color: golden, bronze
coffin accessory D023B
coffin cross
Material : zinc alloy
Color: golden, bronze
Min Qty:10000pcs
More information:
| Zamak 2 properties | ||
| Property | Metric value | Imperial value |
| Mechanical properties | ||
| Ultimate tensile strength | 397 MPa (331 MPa aged) | 58,000 psi |
| Yield strength (0.2% offset) | 361 MPa | 52,000 psi |
| Impact strength | 38 J (7 J aged) | 28 ft-lbf (5 ft-lbf aged) |
| Elongation at Fmax | 3% (2% aged) | |
| Elongation at fracture | 6% | |
| Shear strength | 317 MPa | 46,000 psi |
| Compressive yield strength | 641 MPa | 93,000 psi |
| Fatigue strength (reverse bending 5x108 cycles) | 59 MPa | 8,600 psi |
| Hardness | 130 Brinell (98 Brinell aged) | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Physical properties | ||
| Solidification range (melting range) | 379—390 °C | 714—734 °F |
| Density | 6.8 kg/dm3 | 0.25 lb/in3 |
| Coefficient of thermal expansion | 27.8 μm/m-°C | 15.4 μin/in-°F |
| Thermal conductivity | 105 W/m-K | 729 BTU-in/hr-ft2-°F |
| Electrical resistivity | 6.85 μΩ-cm at 20 °C | 2.70 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10−5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |
Zamak 3 properties
| Property | Metric value | Imperial value |
| Mechanical properties | ||
| Ultimate tensile strength | 268 MPa | 38,900 psi |
| Yield strength (0.2% offset) | 208 MPa | 30,200 psi |
| Impact strength | 46 J (56 J aged) | 34 ft-lbf (41 ft-lbf aged) |
| Elongation at Fmax | 3% | |
| Elongation at fracture | 6.3% (16% aged) | |
| Shear strength | 214 MPa | 31,000 psi |
| Compressive yield strength | 414 MPa | 60,000 psi |
| Fatigue strength (reverse bending 5x108 cycles) | 48 MPa | 7,000 psi |
| Hardness | 97 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Physical properties | ||
| Solidification range (melting range) | 381—387 °C | 718—729 °F |
| Density | 6.7 g/cm3 | 0.24 lb/in3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 113 W/mK | 784 BTU-in/hr-ft2-°F |
| Electrical resistivity | 6.37 μΩ-cm at 20 °C | 2.51 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10−5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.07 | |