Product Details:
|
| Material: | Zinc Alloy | Size: | 12.5*16 |
|---|---|---|---|
| Usage: | Funeral Decoration | ||
| High Light: | cross crucifix,catholic cross |
||
Zamak Jesus Part Funeral Accessory Bronze Color Size 12.5*16cm Material Zinc Alloy
Main information:
Product name: Funeral accessory
Model: J01
Brand: B&R
Application: Funeral decoration
Origin: China
Manufacturer: Sumer International (Beijing) Trading Co.,Ltd
Product detail:
Size: 12.5*16 cm
Material: Zamak (Zinc alloy)
Color: Gold, Silver or Bronze (Optional)
Curved backside for tightly attached on urn
MOQ:1000 pcs
Main feature:
Professionally engaged in funeral field over 10 years;
Customized products acceptable;
Good quality and competitive price;
MORE INFORMATION:
amak 3
Zamak 3 is the de facto standard for the zamak series of zinc alloys; all other zinc alloys are compared to this. Zamak 3 has the base composition for the zamak alloys (96% zinc, 4% aluminium). It has excellent castability and long term dimensional stability. More than 70% of all North American zinc die castings are made from zamak 3.
Zamak 3 composition per standard
| Alloying elements | Impurities | |||||||||||
| Standard | Limit | Al | Cu† | Mg | Pb | Cd | Sn | Fe | Ni | Si | In | Tl |
| ASTM B240 (Ingot) | min | 3.9 | - | 0.025 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.1 | 0.05 | 0.004 | 0.003 | 0.002 | 0.075 | - | - | - | - | |
| ASTM B86 (Cast) | min | 3.5 | - | 0.025 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.25 | 0.05 | 0.005 | 0.004 | 0.003 | 0.1 | - | - | - | - | |
| EN1774 (Ingot) | min | 3.8 | - | 0.035 | - | - | - | - | - | - | - | - |
| max | 4.2 | 0.03 | 0.06 | 0.003 | 0.003 | 0.001 | 0.02 | 0.001 | 0.02 | - | - | |
| EN12844 (Cast) | min | 3.7 | - | 0.025 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.1 | 0.06 | 0.005 | 0.005 | 0.002 | 0.05 | 0.02 | 0.03 | - | - | |
| JIS H2201 (Ingot) | min | 3.9 | - | 0.03 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.03 | 0.06 | 0.003 | 0.002 | 0.001 | 0.075 | - | - | - | - | |
| JIS H5301 (Cast) | min | 3.5 | - | 0.02 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.25 | 0.06 | 0.005 | 0.004 | 0.003 | 0.01 | - | - | - | - | |
| AS1881 | min | 3.9 | - | 0.04 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.03 | 0.06 | 0.003 | 0.003 | 0.001 | 0.05 | - | 0.001 | 0.0005 | 0.001 | |
| GB8738-88 | min | 3.9 | - | 0.03 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.1 | 0.06 | 0.004 | 0.003 | 0.0015 | 0.035 | - | - | - | - | |
| †Impurity | ||||||||||||
Zamak 3 properties
| Property | Metric value | Imperial value |
| Mechanical properties | ||
| Ultimate tensile strength | 268 MPa | 38,900 psi |
| Yield strength (0.2% offset) | 208 MPa | 30,200 psi |
| Impact strength | 46 J (56 J aged) | 34 ft-lbf (41 ft-lbf aged) |
| Elongation at Fmax | 3% | |
| Elongation at fracture | 6.3% (16% aged) | |
| Shear strength | 214 MPa | 31,000 psi |
| Compressive yield strength | 414 MPa | 60,000 psi |
| Fatigue strength (reverse bending 5x108 cycles) | 48 MPa | 7,000 psi |
| Hardness | 97 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Physical properties | ||
| Solidification range (melting range) | 381—387 °C | 718—729 °F |
| Density | 6.7 g/cm3 | 0.24 lb/in3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 113 W/mK | 784 BTU-in/hr-ft2-°F |
| Electrical resistivity | 6.37 μΩ-cm at 20 °C | 2.51 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10−5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.07 | |
Zamak 4
Zamak 4 was developed for the Asian markets to reduce the effects of die soldering while maintaining the ductility of zamak 3. This was achieved by using half the amount of copper from the zamak 5 composition.
Zamak 4 composition per standard
| Alloying elements | Impurities | |||||||||||
| Standard | Limit | Al | Cu | Mg | Pb | Cd | Sn | Fe | Ni | Si | In | Tl |
| Ningbo Jinyi Alloy Material Co. | min | 3.9 | 0.3 | 0.03 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.5 | 0.06 | 0.003 | 0.002 | 0.002 | 0.075 | - | - | - | - | |
| Genesis Alloys Ltd. | min | 3.9 | 0.3 | 0.04 | - | - | - | - | - | - | - | - |
| max | 4.2 | 0.4 | 0.05 | 0.003 | 0.002 | 0.001 | 0.02 | 0.001 | 0.02 | 0.0005 | 0.001 | |
Zamak 4 properties
| Property | Metric value | Imperial value |
| Mechanical properties | ||
| Ultimate tensile strength | 317 MPa | 46,000 psi |
| Yield strength (0.2% offset) | 221—269 MPa | 32,000—39,000 psi |
| Impact strength | 61 J (7 J aged) | 45 ft-lbf (5 ft-lbf aged) |
| Elongation | 7% | |
| Shear strength | 214—262 MPa | 31,000—38,000 psi |
| Compressive yield strength | 414—600 MPa | 60,000—87,000 psi |
| Fatigue strength (rotary bending 5x108 cycles) | 48—57 MPa | 7,000—8,300 psi |
| Hardness | 91 Brinell | |
| Physical properties | ||
| Solidification range (melting range) | 380—386 °C | 716—727 °F |
| Density | 6.6 g/cm3 | 0.24 lb/in3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 108.9—113.0 W/m-K @ 100 °C | 755.6—784.0 BTU-in/hr-ft2-°F @ 212 °F |
| Electrical conductivity | 26-27% IACS | |
| Specific heat capacity | 418.7 J/kg-°C | 0.100 BTU/lb-°F |