|Material:||Zamak（zinc Alloy）||Origin:||China (Italy Quality)|
|Length:||1 Meter||Other Color:||Gold,Silver,Copper|
Product name:ZAMAK COFFIN HANDLE
Application: European style coffin
Manufacturer: Sumer International (Beijing) Trading Co.,Ltd
Length: 1 meter,3 base
Material: Zamak (Zinc alloy)
Color: Gold, Silver,Bronze or copper (Optional)
Attached on coffin by screw
Professionally engaged in funeral field over 10 years;
Customized products acceptable;
Good quality and competitive price;
Centuries before zinc was discovered in the metallic form, its ores were used for making brass and zinc compounds for medicinal purposes. Zinc compounds were in the ores smelted certainly as early as 200 B.C. to obtain copper and which gave alloys of copper and zinc – the brass family. The Romans certainly were major users of brass. The Greeks also appeared to know zinc, even if not by name.
Zinc alloy standards per country
|Traditional name||Short composition name||Form||Common||ASTM||Short European designation||JIS||China||UK BS 1004||France NFA 55-010||Germany DIN 1743-2||UNS||Other|
|ZnAl4Cu3||Ingot||Alloy 2||AC 43A||ZL0430||-||ZX04||-||Z-A4U3||Z430||Z35540||ZL2, ZA-2, ZN-002|
|Cast||ZP0430||-||Z35541||ZP2, ZA-2, ZN-002|
|Zamak 3||ZnAl4||Ingot||Alloy 3||AG 40A||ZL0400||Ingot type 2||ZX01||Alloy A||Z-A4||Z400||Z35521||ZL3, ZA-3, ZN-003|
|Cast||ZP0400||ZDC2||-||Z33520||ZP3, ZA-3, ZN-003|
|Zamak 4||Ingot||Used in Asia only||ZA-4, ZN-004|
|Zamak 5||ZnAl4Cu1||Ingot||Alloy 5||AC 41A||ZL0410||Ingot type 1||ZX03||Alloy B||Z-A4UI||Z410||Z35530||ZL5, ZA-5, ZN-005|
|Cast||ZP0410||ZDC1||-||Z35531||ZP5, ZA-5, ZN-005|
|Zamak 7||ZnAl4Ni||Ingot||Alloy 7||AG 40B||-||-||ZX02||Z33522||ZA-7, ZN-007|
The Short European Designation code breaks down as follows (using ZL0430 as the example):
Z is the material (Z=Zinc)
P is the use (P=Pressure die casting (casting), L=Ingot)
04 is the percent aluminium (04= 4% aluminium)
3 is the percent copper (3= 3% copper)
ZAMAK 3: This is the most used general purpose zinc die casting alloy, providing an excellent combination of strength, ductility and impact strength. It also provides excellent plating and finishing characteristics. This alloy is the designer's first choice for die casting applications.
ZAMAK 5: ZAMAK 5 should be considered when moderately greater hardness, strength and creep resistance over ZAMAK 3 is required.
ZAMAK 7: this is a high purity for of ZAMAK 3 with similar mechanical properties. However, ZAMAK 7 has higher ductility (for forming bending operations) and the highest casting fluidity of the ZAMAK family.