Product Details:
|
| Material: | Metal Zinc Alloy | Color: | Gold Silver Or Bronze |
|---|---|---|---|
| Spec: | 96/128mm | ||
| High Light: | Furniture Knobs And Pulls,Furniture Pulls And Handles |
||
Brand: Leya
Product Number: 6007
Type: Simple style
Usage: Cabinet,drawer, dresser kitchen or other furniture hardware use.
Color: Gold Silver Bronze and others
Surface : Satin Nickel/Chrome Plated (Special color negotiable)
Central space: 96 / 128 mm as the default
Weight: 40-54g (for your reference)
Good quality and reasonable price.
Manufactured by : Wenzhou Leya Metal Hardware Co.,Ltd
The subsidiary of Sumer International (Beijing) Trading Co.,Ltd
Customized design welcome!
Apperance of Product No 6007 zinc alloy office furniture handle
MORE INFORMATION:
| Zamak 2 properties | ||
| Property | Metric value | Imperial value |
| Mechanical properties | ||
| Ultimate tensile strength | 397 MPa (331 MPa aged) | 58,000 psi |
| Yield strength (0.2% offset) | 361 MPa | 52,000 psi |
| Impact strength | 38 J (7 J aged) | 28 ft-lbf (5 ft-lbf aged) |
| Elongation at Fmax | 3% (2% aged) | |
| Elongation at fracture | 6% | |
| Shear strength | 317 MPa | 46,000 psi |
| Compressive yield strength | 641 MPa | 93,000 psi |
| Fatigue strength (reverse bending 5x108 cycles) | 59 MPa | 8,600 psi |
| Hardness | 130 Brinell (98 Brinell aged) | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Physical properties | ||
| Solidification range (melting range) | 379—390 °C | 714—734 °F |
| Density | 6.8 kg/dm3 | 0.25 lb/in3 |
| Coefficient of thermal expansion | 27.8 μm/m-°C | 15.4 μin/in-°F |
| Thermal conductivity | 105 W/m-K | 729 BTU-in/hr-ft2-°F |
| Electrical resistivity | 6.85 μΩ-cm at 20 °C | 2.70 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10−5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |
The name zamak is an acronym of the German names for the metals of which the alloys are composed: Zink (zinc), Aluminium, Magnesium and Kupfer (copper).The New Jersey Zinc Company developed zamak alloys in 1929. Zinc alloys are popularly referred to as pot metal or white metal. While zamak is held to higher industrial standards, it is still considered a pot metal.
The Short European Designation code breaks down as follows (using ZL0430 as the example):
Z is the material (Z=Zinc)
P is the use (P=Pressure die casting (casting), L=Ingot)
04 is the percent aluminium (04= 4% aluminium)
3 is the percent copper (3= 3% copper)
Zinc alloy standards per country
| Traditional name | Short composition name | Form | Common | ASTM | Short European designation | JIS | China | UK BS 1004 | France NFA 55-010 | Germany DIN 1743-2 | UNS | Other | ||
| Zamak 2 or Kirksite | ZnAl4Cu3 | Ingot | Alloy 2 | AC 43A | ZL0430 | - | ZX04 | - | Z-A4U3 | Z430 | Z35540 | ZL2, ZA-2, ZN-002 | ||
| Cast | ZP0430 | - | Z35541 | ZP2, ZA-2, ZN-002 | ||||||||||
| Zamak 3 | ZnAl4 | Ingot | Alloy 3 | AG 40A | ZL0400 | Ingot type 2 | ZX01 | Alloy A | Z-A4 | Z400 | Z35521 | ZL3, ZA-3, ZN-003 | ||
| Cast | ZP0400 | ZDC2 | - | Z33520 | ZP3, ZA-3, ZN-003 | |||||||||
| Zamak 4 | Ingot | Used in Asia only | ZA-4, ZN-004 | |||||||||||
| Zamak 5 | ZnAl4Cu1 | Ingot | Alloy 5 | AC 41A | ZL0410 | Ingot type 1 | ZX03 | Alloy B | Z-A4UI | Z410 | Z35530 | ZL5, ZA-5, ZN-005 | ||
| Cast | ZP0410 | ZDC1 | - | Z35531 | ZP5, ZA-5, ZN-005 | |||||||||
| Zamak 7 | ZnAl4Ni | Ingot | Alloy 7 | AG 40B | - | - | ZX02 | Z33522 | ZA-7, ZN-007 | |||||
Contact Person: Ms. Helen Ren
Tel: +86-13801202918
Fax: 86-10-67163945