Product Details:
|
| Material: | Metal Zinc Alloy | Color: | Gold Silver Or Bronze |
|---|---|---|---|
| Spec: | 96/128mm | ||
| High Light: | Furniture Knobs And Pulls,Furniture Pulls And Handles |
||
Brand: Leya
Product Number: 6013
Type: Simple style
Usage: Cabinet,drawer, dresser kitchen or other furniture hardware use.
Color: Gold Silver Bronze and others
Surface :Nickel plated/Gold/Satin Nickel
(Special color negotiable)
Central distance: 64 / 96 / 128 mm as standard
Weight: 40-92g (for your reference)
Good quality and reasonable price.
Manufactured by : Wenzhou Leya Metal Hardware Co.,Ltd
The subsidiary of Sumer International (Beijing) Trading Co.,Ltd
Customized design welcome!
Different handles zinc alloy 6013
clear view of 6013 metal handle
96 and 128 mm metal furniture handle 6013 side look
More info:
Zamak 4
Zamak 4 was developed for the Asian markets to reduce the effects of die soldering while maintaining the ductility of zamak 3. This was achieved by using half the amount of copper from the zamak 5 composition.
Zamak 4 composition per standard
| Alloying elements | Impurities | |||||||||||
| Standard | Limit | Al | Cu | Mg | Pb | Cd | Sn | Fe | Ni | Si | In | Tl |
| Ningbo Jinyi Alloy Material Co. | min | 3.9 | 0.3 | 0.03 | - | - | - | - | - | - | - | - |
| max | 4.3 | 0.5 | 0.06 | 0.003 | 0.002 | 0.002 | 0.075 | - | - | - | - | |
| Genesis Alloys Ltd. | min | 3.9 | 0.3 | 0.04 | - | - | - | - | - | - | - | - |
| max | 4.2 | 0.4 | 0.05 | 0.003 | 0.002 | 0.001 | 0.02 | 0.001 | 0.02 | 0.0005 | 0.001 | |
Zamak 4 properties
| Property | Metric value | Imperial value |
| Mechanical properties | ||
| Ultimate tensile strength | 317 MPa | 46,000 psi |
| Yield strength (0.2% offset) | 221—269 MPa | 32,000—39,000 psi |
| Impact strength | 61 J (7 J aged) | 45 ft-lbf (5 ft-lbf aged) |
| Elongation | 7% | |
| Shear strength | 214—262 MPa | 31,000—38,000 psi |
| Compressive yield strength | 414—600 MPa | 60,000—87,000 psi |
| Fatigue strength (rotary bending 5x108 cycles) | 48—57 MPa | 7,000—8,300 psi |
| Hardness | 91 Brinell | |
| Physical properties | ||
| Solidification range (melting range) | 380—386 °C | 716—727 °F |
| Density | 6.6 g/cm3 | 0.24 lb/in3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 108.9—113.0 W/m-K @ 100 °C | 755.6—784.0 BTU-in/hr-ft2-°F @ 212 °F |
| Electrical conductivity | 26-27% IACS | |
| Specific heat capacity | 418.7 J/kg-°C | 0.100 BTU/lb-°F |